SIFAT KIMIA
| CU | SI | Fe | M N | mg | ZN |
|---|---|---|---|---|---|
| 0,25 persen | 0,30 persen | 0,maks 70 persen | 1-1,50 persen | 0.80-1,30 persen | 0,25 persen |
PERALATAN MEKANIS
| NILAI | KEKUATAN (METRIK/IMPERIAL) | PEMANJANGAN | KEKERASAN | |||
|---|---|---|---|---|---|---|
| Melunakkan | Kekuatan tekanan maksimum | Kekuatan Hasil Tertinggi | Kekuatan Geser | Kekuatan Kelelahan | persen | Brinell |
| 3004-O | 180 MPa / 26,000 psi | 69 MPa / 10,000 psi | 110 MPa / 16,000 psi | 97 MPa / 14,000 psi | 20-25 | 45 |
| 3004-H34 | 215 MPa / 31,000 psi | 170 MPa / 25,000 psi | 115 MPa / 17,000 psi | 105 MPa / 15,000 psi | 10-17 | 52 |
| 3004-H36 | 240 MPa / 35,000 psi | 200 MPa / 25,000 psi | 125 MPa / 18,000 psi | 105 MPa / 15,000psi | 9-12 | 63 |
| 3004-H36 | 260 MPa / 38,000 psi | 230 MPa / 33,000 psi | 140 MPa / 20,000 psi | 110 MPa / 16,000 psi | 5-9 | 70 |
| 3004-H38 | 285 MPa / 41,000 psi | 250 MPa / 36,000 psi | 145 MPa / 21,000 psi | 110 MPa / 16,000 psi | 4-6 | 77 |
PERTANYAAN YANG SERING DITANYAKAN
APA PERBEDAAN ANTARA ALUMINIUM 3003 DAN 3004?APAKAH ALUMINIUM 3004 DIGUNAKAN UNTUK PERANGKAT MASAK?APA KEGUNAAN 3004?
Apa perbedaan antara aluminium 3003 dan 3004?
MENJAWAB:
Kedua paduan serba guna ini sangat mirip. Dalam hal komposisi kimianya, aluminium 3004 memiliki tambahan magnesium yang menjadikan kelas ini lebih unggul dalam hal kekuatan.